SUNLU Engineering Filament Collection Easy PA, PC-ABS, PA6-CF, PA12-CF, PA6-GF | SUNLU UK Online Store
Key Features
- Carbon Fiber Reinforced Nylon (PA6-CF)
20% carbon fiber delivers exceptional stiffness, strength, and dimensional stability - Extreme Heat Resistance up to 209ยฐC
Maintains structural integrity under high temperatures, ideal for demanding environments - Industrial-Grade Strength & Reliability
Excellent layer adhesion with high tensile, torsional, and impact resistance for functional parts
Diameter: 1.75ยฑ0.02mm
Printing Temperature:
- 270-280โ๏ผ50-100mm/s
Bed Temperature:
- 50โ70ยฐC: apply glue
Bubbles: 100% zero bubbles
Net Weight: 1 kg/spool
Gross Weight: 1.3 kg/spool
Length: 1.75 mm (1 kg) โ 358 m
- Free shipping to most of UK regions
- Guaranteedย Secureย Checkout
![[MOQ: 6 Bottles] Water-Wash ABS-Like Resin 1000G](http://uk.store.sunlu.com/cdn/shop/files/MothersDay_ABS_LIKE_WATAR_WASH.jpg?v=1777517048&width=1420)
SUNLU Nylon-6 Carbon Fiber (PA6-CF) Filament
SUNLU PA6-CF nylon filament combines 80% PA with 20% carbon fiber, delivering remarkable stiffness, strength, and heat resistance. It offers excellent layer adhesion, making it ideal for demanding applications. ย
Engineered for strength and durability, SUNLU PA6-CF filament is suitable for industrial uses that require high torsional, tensile, and impact resistance. Ideal applications include gears, screws, helmets, fan blades, toy car chassis, skateboard parts, and bicycle frames. ย
High Strength & Rigidity: Carbon fiber reinforcement significantly increases stiffness, reducing deformation even under mechanical stress.
With a heat distortion temperature of up to 209ยฐC, significantly higher than Easy PA, PC, or ASA, PA6-CF is ideal for high-temperature applications like automotive exhaust pipes, motor covers, pot handles, and kettle bases. ย
[Important Notes]ย
1. Dry the filament before use: 80ยฐC for 24 hours or 110ยฐC for 4 hours. ย
2. Use an abrasion-resistant nozzle (e.g., hardened steel) to prevent wear caused by the filament's carbon fiber content. ย
| Recommended Printing Settings | |
|---|---|
| Drying Settings (Blast Drying Oven) | 80-110โ |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 270-290โ |
| Bed Temperature (With Glue) | 50 - 70 ยฐC |
| Printing Speed | 50mm- 100 mm/s |
| Physical Properties | |
|---|---|
| Density | 1.12 g/cmยณ |
| Vicat Softening Temperature | / |
| Heat Deflection Temperature | 203ยฑ3ยฐC |
| Melting Temperature | 225ยฐC |
| Melt Index | 16.5ยฑ3 g/10 min |
| Mechanical Properties | |
|---|---|
| Tensile Strength | 112ยฑ10 MPa |
| Breaking Elongation Rate | 12ยฑ3% |
| Flexural Strength | 192ยฑ20 MPa |
| Flexural Modulus | 8600ยฑ400 MPa |
| Impact Strength(X-Y) | 6.5ยฑ2 kJ/mยฒ |
Download