Nylon-6 Glass Fiber (PA6-GF) 3D Printer Filament 1KG
Key Features
- 25% Glass Fiber Reinforced PA6
Exceptional stiffness, toughness, and dimensional stability for demanding industrial parts - Extreme Heat Resistance up to 214°C (417°F)
Maintains strength and rigidity in high-temperature environments like automotive and industrial tooling - Chemical-Resistant, Industrial-Grade Durability
Excellent resistance to fuels, acids, and solvents with strong layer adhesion for long-lasting performance
Diameter: 1.75±0.03mm
Printing Temperature:
- 270-290℃：50-120mm/s
Bed Temperature:
- 50–70°C: apply glue
Bubbles: 100% zero bubbles
Net Weight: 1 kg/spool
Gross Weight: 1.3 kg/spool
Length: 1.75 mm (1 kg) ≈ 358 m
- Free shipping to most of UK regions
- Guaranteed Secure Checkout
SUNLU Nylon-6 Grass Fiber (PA6-GF) Filament
PA6 with 25% glass fiber content, High Temp Resistance 417°F(214°C). Engineered Spool System: Features a reusable, heat-resistant spool designed for direct drying. Withstand drying temperatures up to 230°F (110°C) to ensure optimal filament performance right on the reel.
Defy Extreme Heat
Engineered to maintain structural integrity and stiffness at sustained temperatures up to 417°F (214°C). The premier choice for under-hood automotive parts, electrical enclosures, and high-temperature industrial tooling
Superior Chemical Defense
Formulated with 25% glass fibers for exceptional resistance against aggressive acids, fuels, and industrial solvents. Built for demanding applications like chemical valving, fuel systems, and corrosion-vulnerable industrial equipment
Essential Printing Protocol
DRYING IS CRITICAL: Dry for 4 hours at 110°C immediately upon opening and if exposed >6 hours.
Secure Bed Adhesion: Apply bed adhesive (e.g., glue stick) to prevent warping.
Protect Your Nozzle: Copper nozzles wear rapidly. Mandatory: Use abrasion-resistant nozzles (e.g., hardened steel).
| Recommended Printing Settings | |
|---|---|
| Drying Settings (Blast Drying Oven) | 80-110℃ |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 270-290℃ |
| Bed Temperature (With Glue) | 60-70℃ |
| Printing Speed | <130 mm/s |
| Physical Properties | |
|---|---|
| Density | 1.269 g/cm³ |
| Vicat Softening Temperature | / |
| Heat Deflection Temperature | 205.2±3°C |
| Melting Temperature | 225°C |
| Melt Index | 12.2±3 g/10 min |
| Mechanical Properties | |
|---|---|
| Tensile Strength | 89±8 MPa |
| Breaking Elongation Rate | 12.5±3% |
| Flexural Strength | 176±8 MPa |
| Flexural Modulus | 6130±300 MPa |
| Impact Strength(X-Y) | 10.5±2.5 kJ/m² |
Download