PLA-CF, PLA Carbon Fiber 3D Printer Filament 1KG
Key Features
- 15% Carbon Fiber Reinforced Strength
- Matte Professional Finish
- Smooth & Reliable Printing
- High Compatibility & Precision
Printing Temperature: - 215-225℃：50 -100mm/s
- 225-245℃：100 -200mm/s
Bed Temperature:
- When unheated: apply glue
- When heated to 50–60°C: no glue needed
Bubbles: 100% zero bubbles
Net Weight: 1 kg/spool
Gross Weight: 1.3 kg/spool
Length: 1.75 mm (1 kg) ≈ 300 m
- Free shipping to most of UK regions
- Guaranteed Secure Checkout
SUNLU PLA Carbon Fiber (PLA-CF) Filament
15% carbon fiber reinforced PLA delivers enhanced rigidity, warp-free stability, and a premium matte finish. Smooth, low-stringing printing with precise ±0.02mm accuracy—perfect for strong functional parts and refined design projects.
Infused with 15% carbon fiber to significantly increase rigidity and structural strength compared to standard PLA. Delivers excellent dimensional stability and warp-free performance, making it ideal for functional parts, mechanical components, and load-bearing prints.
Engineered to produce a refined frosted matte surface that naturally hides layer lines and enhances visual texture. Perfect for high-end models, display pieces, and projects requiring a sleek, industrial-grade appearance.
Manufactured with ±0.02mm diameter accuracy for stable extrusion and precise detail reproduction. Vacuum-sealed with desiccant to protect against moisture, ensuring dependable performance across most 1.75mm FDM 3D printers.
| Recommended Printing Settings | |
|---|---|
| Drying Settings (Blast Drying Oven) | 50℃ |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 215-225℃: 50-100mm/s; 225-245℃: 100-200mm/s; |
| Bed Temperature | When heated to 50–60°C, no glue needed |
| Printing Speed | 50-100; 100-200mm/s |
| Physical Properties | |
|---|---|
| Density | 1.23 g/cm³ |
| Vicat Softening Temperature | 54°C |
| Heat Deflection Temperature | 55.5±3°C |
| Melting Temperature | 168.6°C |
| Melt Index | 20.4±3 g/10 min |
| Mechanical Properties | |
|---|---|
| Tensile Strength | 44±5 MPa |
| Breaking Elongation Rate | 10.4±3% |
| Flexural Strength | 79±5 MPa |
| Flexural Modulus | 3221±200 MPa |
| Impact Strength(X-Y) | 3.5±1.5 kJ/m² |