[Min. 3 Rolls] High Speed Collection, High Speed PLA, PLA+, PLA+2.0, Matte PLA, Matte PETG, PLA Marble Filament 1KG
Key Features:
- Supports ultra-fast printing up to 600 mm/s
- Excellent flow—smooth, clog-free printing even at high speed (30 mm³/s)
- High crystallization temperature
- Low shrinkage rate. Neatly lined up
Diameter: 1.75±0.02mm
Printing Temperature:
- 190-210℃ 50-150mm/s
- 210-230℃ 150-300mm/s
- 230-260℃ 300-600mm/s
Bed Temperature: 50 - 60℃
Net Weight: 1 kg/spool
Gross Weight: 1.3 kg/spool
Length: 1.75 mm (1 kg) = 330 m
- Free shipping to most of UK regions
- Guaranteed Secure Checkout
SUNLU High-speed PLA Plus
Supports ultra-fast printing up to 600 mm/s, with high toughness, impact resistance, and excellent flow for smooth, flawless prints.. SUNLU-owned tech has mastered advanced technology and produced 100% Neatly Wound PLA PLUS/PLA+ Filament, which is impossible for other brands. No knot, no winding, improve printing efficiency.
Good comprehensive mechanical properties
Particularly drop-resistant, impact strength up to 8KJ/m2, which is 2~3 times more than other PLA or PLA+ on the market, the color is brighter, and it has many advantages, Clog/Bubble/Tangle/Warping/Stringing free, easy to use, better layer adhesion.
Heat dissipation performance
The performance of Highspeed PLA increased by 180%, with faster cooling under the same conditions, and fast printing without piling up materials.
Stable Printing Performance
Low shrinkage and uniform diameter (±0.02 mm) ensure smooth feeding and reliable printing results. Works perfectly with most FDM 3D printers (Bambu Lab, Creality, Prusa, Anycubic, etc.).
| Recommended Printing Settings | |
|---|---|
| Drying Settings (Blast Drying Oven) | 50–55℃ 6–8h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 210-230℃ / ≤400mm/s |
| Bed Temperature | 50-60℃ |
| Printing Speed | ≤400mm/s |
| Physical Properties | |
|---|---|
| Density | 1.27 g/cm³ |
| Vicat Softening Temperature | / |
| Heat Deflection Temperature | 56±3 °C |
| Melting Temperature | 164 °C |
| Melt Index | 7.3±2 g/10 min |
| Mechanical Properties | |
|---|---|
| Tensile Strength | 38±5 MPa |
| Breaking Elongation Rate | 10±3% |
| Flexural Strength | 72±5 MPa |
| Flexural Modulus | 3300±200 MPa |
| Impact Strength | 6±2 kJ/m² |
| Color | Hex Code | Display |
|---|---|---|
| Black | #26282a | |
| White | #ffffff | |
| Grey | #54565a | |
| Red | #bb4041 | |
| Blue | #2556bc | |
| Yellow | #fff13f | |
| Green | #1daa27 | |
| Olive Green | #5a6d3d | |
| Pink | #e67c99 | |
| Orange | #ef8646 |