[MOQ: 3 Rolls] PLA Meta Filament 1KG
Couldn't load pickup availability
Key Features
- High flow for fast, clog-free printing.
- Prints 10°C lower than standard PLA—more energy-efficient.
- Strong and tough—resists drops and cracking.
- Soft macaron colors with smooth, low-layer-line surfaces.
Diameter: 1.75 ± 0.02 mm
Printing Temperature:
- 185–195℃: 50–100 mm/s
- 195–225℃: 100–200 mm/s
Bed Temperature:
- When unheated: glue is required
- When heated to 50–60°C: no glue needed
Net Weight: 1 kg/spool
Gross Weight: 1.3 kg/spool
Length: 1.75 mm (1 kg) = 330 m
- Free shipping to most of UK regions
- Guaranteed Secure Checkout
SUNLU PLA META-High Speed Printing with Low temp
SUNLU 1.75mm PLA Meta 3D printer filament(± 0.02mm Tolerance)smooth squeeze. PLA Meta filament is 1.5 times more fluid than regular PLA. Minimum tolerance and low warping to ensure consistent feeding and fast prints, say goodbye to clogging.
High toughness and non-brittle PLA Meta filament printed parts can be sanded, drilled, and painted. SUNLU PLA Meta filament is very tough and not easily brittle, the model does not break easily when dropped from a height to the ground.
Brightly colored PLA Meta 3d printer filaments bring glossy surface prints to arts, crafts, and 3D projects. SUNLU PLA Meta filament 1.75mm has the advantages of high purity with good adhesion and superb layer bonding.
High Compatiblity & Vacuum Pack
Compatible with 99% FDM 3D printers (with heated beds) and 3D pen. Vacuum neatly arranged SUNLU PLA META 3d printer filament, providing better printing results. Environmental protection, PLA META is made from starch raw materials derived from renewable plant resources.
| Recommended Printing Settings | |
|---|---|
| Drying Settings (Blast Drying Oven) | 50 °C |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 185 - 195 °C / 195 - 225 °C |
| Bed Temperature (with Glue) | 50 - 60 °C |
| Printing Speed | 50 - 100 mm/s / 100 - 200 mm/s |
| Physical Properties | |
|---|---|
| Density | 1.22 g/cm³ |
| Vicat Softening Temperature | 54 °C |
| Heat Deflection Temperature | 57.2 °C |
| Melting Temperature | 164 °C |
| Melt Index | 6.0 g/10 min |
| Mechanical Properties | |
|---|---|
| Tensile Strength | 53 MPa |
| Breaking Elongation Rate | 30 % |
| Flexural Strength | 85 MPa |
| Flexural Modulus | 2500 MPa |
| Impact Strength | 9.1 kJ/m² |
Download